MAGNETIC CHARACTERISTICS AND PHYSICAL PROPERTIES OF INJECTION FERRITE | |||||||||||
GRADE | Binder | Br | Hcb | Hcj | (BH)max | Mold density (g/cm3) | Melt flow rate | Flexual strength | Flexual modulus | ||
Gs | mT | Oe | Oe | MGOe | g/10min(MI) | condition | Mpa(kg/cm2) | Gpa(kg/cm2) | |||
DMS121-A | PA6 | 2900 | 290 | 2500 | 3100 | 2.1 | 3.65 | 100 | 270℃ 10kg | 157.1 | 26.8 |
DMS121-B | PA6 | 2850 | 285 | 2500 | 3150 | 1.95 | 3.6 | 70 | 270℃ 10kg | 165.5 | 25.9 |
DMS121-C | PA6 | 2750 | 275 | 2400 | 2900 | 1.8 | 3.53 | 60 | 270℃ 10kg | 145.8 | 20.1 |
DMS121-D | PA6 | 2550 | 255 | 2350 | 2800 | 1.6 | 3.45 | 60 | 270℃ 10kg | 154.7 | 22.3 |
DMS121-E | PA6 | 1225 | 122.5 | 1150 | 2150 | 0.37 | 2.3 | 150 | 270℃ 10kg | 120.5 | 28.6 |
DMS121-F | PA6 | 1550 | 155 | 1350 | 3100 | 0.64 | 2.55 | 140 | 270℃ 10kg | 115.8 | 27.8 |
DMS121-J | PA6 | 2850 | 285 | 2250 | 2600 | 2 | 3.6 | 70 | 270℃ 10kg | 160 | 26.2 |
DMS121-T | PA6 | 2300 | 230 | 2000 | 3000 | 1.5 | 3 | 80 | 270℃ 10kg | 139.8 | 27.5 |
DMS221-A | PA12 | 2750 | 275 | 2300 | 2400 | 1.85 | 3.4 | 60 | 270℃ 10kg | 162 | 25.2 |
DMS221-B | PA12 | 2820 | 282 | 2600 | 3300 | 2 | 3.6 | 50 | 270℃ 10kg | 162 | 25.2 |
MAGNETIC CHARACTERISTICS AND PHYSICAL PROPERTIES OF INJECTION FERRITE | ||||||||||||||||||
GRADE | Binder resin | Br | Hcb | Hcj | (BH)max | Mold density | Melt flow rate | Flexual strength | Flexual modulus | Tensile strength | Elangation | Impact strength | Shrinkage | |||||
Gs | mT | Oe | kA/m | Oe | kA/m | MGOe | Kj/m3 | (g/cm3) | g/10min(MI) | condition | Mpa(kg/cm2) | Gpa(kg/cm2) | Mpa | % | kj/m2 | % | ||
TP-S62 | PA6 | 2390 | 239 | 2140 | 170 | 2900 | 230.8 | 1.4 | 11.14 | 3.27 | 100 | 270℃ -10kg | 189 1927 | 15.8 1.6E+05 | 99.5 1015 | 4.6 | NB NB | 0.75 |
TP-S65 | PA6 | 2750 | 275 | 2350 | 187 | 2780 | 221.2 | 1.87 | 14.88 | 3.63 | 135 | 270℃ -10kg | 167 1703 | 23 2.3E+05 | 79.1 807 | 3.0 | 11.9 12.1 | 0.57 |
TP-S67K | PA6 | 2900 | 290 | 2280 | 180 | 2650 | 210.9 | 2.07 | 16.5 | 3.73 | 70 | 270℃ -10kg | 182 1856 | 27.5 2.8E+05 | 97.6 995 | 3.4 | 13.5 13.7 | 0.41 |
TP-F26S | PA12 | 2820 | 282 | 2360 | 188 | 2870 | 228.4 | 1.96 | 15.6 | 3.63 | 65 | 270℃ -10kg | 115 1173 | 14.5 1.5E+05 | 59.1 603 | 3.9 | 15.6 15.9 | 0.66 |
TP-A27E | PA12 | 2890 | 289 | 2390 | 190 | 2880 | 229.2 | 2.05 | 16.2 | 3.69 | 65 | 270℃ -10kg | 92 938 | 11.3 1.2E+05 | 45.6 465 | 5.3 | 20.4 20.8 | 0.72 |
TP-S76 | PPS | 2360 | 236 | 2160 | 172 | 3060 | 243 | 1.38 | 11 | 3.33 | 160 | 270℃ -10kg | 149 1522 | 13.9 1.4E+05 | 73.7 751 | 2.5 | 20.6 21.0 | 0.6 |
MAGNETIC CHARACTERISTICS AND PHYSICAL PROPERTIES OF INJECTION FERRITE | |||||||||||||||||
GRADE | Br | Hcb | Hcj | (BH)max | Mold density (g/cm3) | Melt flow rate | Moisture | Flexual strength | Tensile strength | Impact strength | Shrinkage | Heat distorsion temp. | Coefficent of linear expansion | ||||
Gs | mT | Oe | kA/m | Oe | kA/m | MGOe | Kj/m3 | g/10min | ppm | Mpa(kg/cm2) | Mpa | kj/m2 | % | ℃ | 1/℃ | ||
L240 | 4540 | 454 | 3830 | 305 | 8680 | 691 | 4.4 | 35 | 4.69 | 463 | 68 | 118.3 | 26.4 | 0.6 | 0.6 | 143 | 5.5OE-05 |
L250 | 5070 | 507 | 4250 | 338 | 8710 | 693 | 5.4 | 43 | 5.01 | 470 | 36 | 115 | 17.1 | 0.4 | 0.4 | 4.2OE-05 | |
L260 | 5563 | 556 | 4550 | 362 | 9010 | 717 | 6.3 | 50.1 | 5.37 | 477 | 50 | 96 | 10 | 0.4 | 0.4 | 3.80E-05 | |
L270 | 5815 | 582 | 4788 | 381 | 9028 | 718 | 6.9 | 54.9 | 5.57 | 216 | 60 | 93 | 11 | 0.5 | 0.5 | ||
N230 | 3940 | 394 | 3380 | 269 | 9860 | 785 | 3.3 | 26.3 | 3.97 | 468 | 31 | 120 | 37.1 | 0.9 | 0.9 | 7.10E-05 | |
N260 | 5360 | 536 | 4430 | 353 | 9700 | 773 | 5.9 | 47 | 5.02 | 412 | 28 | 121.4 | 17.1 | 0.5 | 0.5 | ||
N270 | 5850 | 585 | 4650 | 370 | 8920 | 710 | 6.8 | 54.1 | 5.28 | 505 | 46 | 114.3 | 13.1 | 0.4 | 0.4 | 151 | 3.50E-05 |
N280S | 6190 | 619 | 4840 | 385 | 8850 | 704 | 7.6 | 59.7 | 5.54 | 773 | 85 | 71.9 | 7.6 | 0.2 | 0.2 | 2.30E-05 |